Product description:
This product is a new lubrication technology, has lubricating effect of waterproof and dustproof and durable, can be used in a wide range of working temperature environment, lubrication efficiency high, all from the saponifiers created by SCS to use the new lubrication technology (Super Calcium Complex). Under the condition of high temperature operation a lot, lubricating effect than the other same level of lubricating oil, does not contain some heavy metals or other environmentally harmful additives, such as sulfide, chloride, zinc phosphide, phenolic compounds, antimony, barium or lead.
Product application:
The application of a wide range of industries, such as automobile industry, construction industry, agriculture, industry, railway, mining operations related to the unique characteristics can be used in all automobile bearings, shaft, and antifriction bearing, high speed of the universal bearing, conveying system of high temperature furnace, electric motor bearings, bearing water resistance the paper mill, steel rolling bearing, textile machine, stretching machine, baking room, bulldozers and mechanical equipment, is also very suitable for humid environment and Fisheries strong corrosion.
Product features:
Mechanical stability and mechanical stability is quite remarkable, shows that after 100000 times after the operation of oil viscosity will not produce any change in ASTM grease stability test, this test (D - 1831) at room temperature with a temperature of 150 DEG C for 6-100 hours of operation, after testing without any softening phenomenon.
Anti extreme pressure - also has good anti pressure (EP properties).Timken OK load LWI of value reaches 65 pounds, 65 kg (weld point) and the fusion point of excellent numerical 500kg, showing the outstanding four ball extreme pressure value.
Oxidation stability - antioxidant stability Bomb oxidation stability(D-942) Shows that after 500 hours there is psi, drop, 2, and 1000 hours with psi, 9, drop values, this value is much better than other peer products.
Water resistance
1.the water stability in a number of ASTM water stability test showed that the mixture of 50% water, and after the 100000 operation, still do not have any change of viscosity, water resistance grease like other brands will serious deterioration or failure.
2. water resistance test - excellent water resistance, recommended for use in pickling or alkaline environments. In this test, it has excellent adhesion ability and high water resistance.
3. Again, the water erosion test (D-1264) emphasizes that the test still doubles its advantages over other products.
Corrosion resistance tests - excellent protection against water which is not available in general products. In the salt fog spray test with amazing strength numerical 4000 hours pass easily through the ASTM D1743 bearing corrosion test, in which a series of tests, with synthetic seawater to do the test, by using a1,1,1 series. Further copper test (Emcore, Test), data for A0, level 0.
Salt spray test-ASTM B 117：5% Salt Fog @ 100℉,5 mils on Q-Panel type S. Soak Test5mils on Q-Panel type S,submerged 50% in a 5% salt solution at room temperature.
Low temperature stability-Super GreaseIt can also be used as a general low temperature grease
There are also fairly good data on tests at low temperatures，U.S.Steel Mobility Test-this is a measure of pumpability and shows good pumpability (U.S.Steel Mobility @ 0℉,0.12 grams per second).
Abstract - a versatile, versatile grease that is stable, ultra efficient, and has no drawbacks or weaknesses. It is a versatile, versatile grease.
- Place of Origin: China
- Brand Name: D XunTong
- Model Number: GU-55
- Weight: 15.000 kg
Product characteristics table
NL GI Grade……………………………………...............………………………… 0-2
Worked Penetration,77℉,ASTM D-217
60 strokes…………………………………....……….…………………………265-380
10,000 strokes change from 60 strokes……………………………………… ±1
100,000 strokes change from 60 strokes……................................................…±2
Color…………………….............………………..…………………………………… Amber
dropping point，℉（℃）Min,ASTM D-2265…………………………………………>630(>340)
Rust resistance，ASTM D-1743…………………………………………………………………Pass
Antioxidant stability，PSI Loss,ASTM D-942
100 hours…………………………………………………………………………… 0
500 hours…………………………………………………………………………… 2
1,000 hours………………………………………………………………………… 9
Operation stability，Penetration Change,ASTM D-1831………………………......… 2
Separation of lipid, 24 hrs@25℃(77℉),ASTM D-1742………………………......…0.17
Four Ball EP,Weld Point,kg ASTM D-2596……………………………....……………500
Four Ball EP,Load Wear Index,kg,ASTM D-2596……………………....………………65
Four Ball Wear,Scar mm,ASTM D-2266………………………………......…………… 0.39
Timken OK Load,Ib,ASTM D-2509………………………………………......…………… 65
Salt spray test，Hour, ASTM B-117…………………………………….......…………… 4000
Water erosion resistance，% Ioss……………………………………………………...... 2.75
Wheel Bearing Leakage,% loss,grams,ASTM D-1263……………….....………………0.4
Fretting Wear Protection,mgsloss,ASTM D-4170
Ambient Temperature…………………………………………….......…………………2.50 @0℉…………………………………………………………………........………………6.20
Characteristic viscosity of base oil:
Characteristic：
@210℉,SUS. …………………………………………….....……………………85 @100℉,
SUS. ………………………………………….......… 1,100(ISO VG 220)
Viscosity index， Min. ………………………………………....…………………… 95
Low temperature flow point，℉………………………………………....………… 5
High and low temperature lubricating oils, greases, special purpose lubricants;